TCr0.7,C18100鉻銅合金板棒化學成分力學性能物理性能
Introduction
UNS C18100 high conductivity chromium zirconium copper alloys are the alloys containing chromium, zirconium and copper in specific amounts. They have good strength at high temperatures and excellent wear resistance property. The following datasheet will discuss in detail about the UNS C18100 copper alloys.
Chemical Composition
The following table shows the chemical composition of UNS C18100 copper alloys.
| Element | Content (%) |
|---|---|
| Cr | 0.6 - 0.80 |
| Cu | ≥ 98.45 |
| Zr | 0.10 - 0.15 |
Physical Properties
The physical properties of UNS C18100 copper alloys are given in the following table.
| Properties | Metric | Imperial |
|---|---|---|
| Density | 8.82 g/cm3 | 0.319 lb/in3 |
Mechanical Properties
The mechanical properties of UNS C18100 copper alloys are tabulated below.
| Properties | Metric | Imperial |
|---|---|---|
| Tensile strength | ≥ 415 MPa | ≥ 60200 psi |
| Yield?strength | ≥ 345 MPa | ≥ 50000 psi |
| Elongation at break | ≥ 25.0% | ≥ 25.0% |
Fabrication and Heat Treatment
Welding
C18100 copper alloys are welded using soldering, brazing, gas shielded arc welding and butt welding. Oxyacetylene welding, seam welding and spot welding are not preferred for this type of alloys.
Forging
C18100 copper alloys are forged at temperatures ranging from 788 to 927°C (1450 to 1700°F).
Hot Working
C18100 copper alloys have excellent hot working property.
Cold Working
C18100 copper alloys have good cold working property.
Annealing
Annealing of C18100 copper alloys is performed at temperatures ranging from 599 to 704°C (1110 to 1300°F).
Applications
The following are the major applications of UNS C18100 copper alloys:
- Welding electrodes
- Electrical components
- Electrical contacts
- Electrical studs