通過顯微硬度測試、常規拉伸性能測試、掃描電鏡和透射電鏡等觀察手段研究Cu含量對含Sc鋁鋰合金顯微組織和力學性能的影響。
Cu含量對含Sc鋁鋰合金顯微組織和力學性能的影響Effects of Cu content on microstructure and mechanical properties of Al-Cu-Li-Sc alloy通過顯微硬度測試、常規拉伸性能測試、掃描電鏡和透射電鏡等觀察手段研究Cu含量對含Sc鋁鋰合金顯微組織和力學性能的影響。結果表明:在Sc元素含量基本不變的情況下，Cu含量為4.2%(質量分數)的合金在均勻化過程中會形成W(AlCuSc)相，且該相在固溶時也不會完全溶解到α(Al)。在相同Sc含量條件下，隨著α(Al)中Cu含量的下降，w(Cu)/w(Sc)變小，均勻化后形成的W相數量會明顯降低，直至消失。由于W相對合金力學性能不利，其數量的減少可以增加合金中有效固溶Cu原子的數量，從而提高合金性能，W相的形成抑制合金中Al3(Sc,Zr)粒子的析出形成。
The effects of Cu content on the microstructure and mechanical properties of Al-Cu-Li-Sc alloys were investigated by microhardness test, tensile test, scanning electron microscopy (SEM) and transmission electron microscopy (TEM) observations. The results indicate that the alloys with high Cu content will precipitate W(AlCuSc) phase during homogenization when the Sc content is same, and the W phase will not dissolve into the α(Al) at solution treatment. The amount of W phase will decrease with the reduction of Cu content while the Sc content is the same. Because of the deleterious effects of W phase on the mechanical properties, the content of Cu atoms in α(Al) improves, the precipitation of θ′ and T1?phases improve the mechanical properties after aging. The formation of Al(Sc,Zr) particles will be inhibited due to the existence of W phase.
作為值得信賴的合作伙伴和高品質金屬合金的半成品供應商，艾荔艾擁有完善的服務體系和專業的團隊。在同客戶交易的過程中，我們力求根據不同的應用需求將我們的產品做到精益求精。針對當前和未來的市場需求，艾荔艾致力于為客戶提供最佳的金屬材料解決方案。
AILIAI has been a reliable partner and supplier of sophisticated and high-quality semi-finished products maed of alloys. In dialogue with our customers, we optimise our products to meet the specific application requirements. AILIAI develops the best alloy material solutions for current and future challenges.
獲取更多我們供應的合金和服務信息，請致電086-021-67660801或發電子郵件kefu@ailiaigroup.com聯系我們，您也可以通過微博，微信，領英，XING，臉書和推特與我們互動。
For more information on the alloys and services that we supply,?call us?at 086-021-67660801 or email us at kefu@ailiaigroup.com. You can also get in touch on social media, we are constantly active on?Weibo,?Weixin,?LinkedIn,?XING,?Facebook?and?Twitter.