TA1/X65鈦-鋼復合板焊接工藝及焊縫組織和性能
發布人：上海艾荔艾合金股份有限公司www.shailiai.cn
更新時間：2016-04-23
采用 TIG+MIG+MAG 焊接工藝對 TA1/ X65 爆炸冶金復合板(復層 Ti 厚 2 mm, 基層 X65 管線鋼厚 14 mm)試件進行了以 V/Cu 作為過渡填充金屬的板-板對接焊實驗. 利用 OM, XRD, EDS 面掃描, 顯微硬度測試和拉伸實驗, 研究了焊縫區組織特征、界面元素分布、主要物相、顯微硬度分布及焊縫力學性能.
TA1/X65鈦-鋼復合板焊接工藝及焊縫組織和性能INVESTIGATION ON THE WELDING PROCESS AND?MICROSTRUCTURE AND MECHANICAL PROPERTY OF BUTT JOINTS?OF TA1/X65 CLAD PLATES?采用 TIG+MIG+MAG 焊接工藝對 TA1/ X65 爆炸冶金復合板(復層 Ti 厚 2 mm, 基層 X65 管線鋼厚 14 mm)試件進行了以 V/Cu 作為過渡填充金屬的板-板對接焊實驗. 利用 OM, XRD, EDS 面掃描, 顯微硬度測試和拉伸實驗, 研究了焊縫區組織特征、界面元素分布、主要物相、顯微硬度分布及焊縫力學性能. 結果表明, 圓弧狀“U”型坡口設計有利于過渡層 Cu 的 MIG 焊接, 在 Cu-鋼界面不會引起應力集中而萌生裂紋. 熔敷金屬 Ti, V,?Cu 和 Fe 有明顯分區, 擴散互融現象不明顯, 各區域間由固溶體相過渡連接, Ti/V 過渡界面組織結構為鈦基固溶體, V/Cu 過渡界面組織結構為釩基固溶體, Cu/Fe 過渡界面組織結構為銅基固溶體. 焊縫硬度較高區域出現在 Ti/V 過渡界面和 V/Cu 過渡界面處, 硬度值達 326 和 336 HV10, 對過渡界面層塑韌性有一定影響. 焊縫抗拉強度可達 558 MPa, 主要由碳鋼層貢獻.?
Titanium/steel clad material with excellent mechanical properties and corrosion resistance has?important application in storage and transportation equipment of oil and gas. Due to the metallurgical?incompatibility of titanium and steel, the mechanical properties of weld joint would completely lose when the?brittle intermetallic phase TixFey?and TiC appeared in the fusion welding process. Therefore, the gas tungsten?arced welding (TIG), metal inert-gas welding (MIG) and metal active-gas welding (MAG) with V/Cu composite?filler metals for butt joint in this study was carried out on TA1/X65 pipeline steel clad plates with thickness 16?mm ( titanium cladding with thickness 2 mm, X65 pipeline steel with thickness 14 mm). The microstructure,?interface element distribution, main phase, microhardness distribution on cross section and mechanical properties?of butt welds were investigated by using OM, XRD, EDS element mapping, microhardness and tensile test. The?results indicate that the design of “U-type” circular groove advantageous to the MIG of Cu transition-metals,?because of the “U-type” circular groove does not cause stress concentration and crack initiation. The deposited?metal of Ti, V, Cu and Fe have obvious zoning, interdiffusion melting phenomenon is not severe, and by using?solid solution phases to transit zonings of deposited metal. The microstructure of Ti and V transition interface was?composed of Ti-based solid solution, the microstructure of V and Cu transition interface was composed of V-based?solid solution, and the microstructure of Cu and Fe transition interface was composed of Cu-based solid solution.?The high hardness region of butt weld cross section appeared in the Ti/V transition-interface and V/Cu?transition-interface, the hardness value was respectively 326 HV10 and 336 HV10, and weakened the ductility of?transition interfacial layer. A joint with a tensile strength of 558 MPa, mainly of that of the carbon steel was?obtained.?
作為值得信賴的合作伙伴和高品質金屬合金的半成品供應商，艾荔艾擁有完善的服務體系和專業的團隊。在同客戶交易的過程中，我們力求根據不同的應用需求將我們的產品做到精益求精。針對當前和未來的市場需求，艾荔艾致力于為客戶提供最佳的金屬材料解決方案。
AILIAI has been a reliable partner and supplier of sophisticated and high-quality semi-finished products maed of alloys. In dialogue with our customers, we optimise our products to meet the specific application requirements. AILIAI develops the best alloy material solutions for current and future challenges.
獲取更多我們供應的合金和服務信息，請致電086-021-67660801或發電子郵件kefu@ailiaigroup.com聯系我們，您也可以通過微博，微信，領英，XING，臉書和推特與我們互動。
For more information on the alloys and services that we supply,?call us?at 086-021-67660801 or email us at kefu@ailiaigroup.com. You can also get in touch on social media, we are constantly active on?Weibo,?Weixin,?LinkedIn,?XING, Facebook?and?Twitter.