在室溫下使用超聲疲勞試驗機對GH4169鎳基高溫合金進行了105~108周次的疲勞試驗, 獲得了S-N曲線并觀察了疲勞斷口形貌。
GH4169鎳基高溫合金的超高周疲勞性能Very High Cycle Fatigue Properties of GH4169 Ni-based Superalloy在室溫下使用超聲疲勞試驗機對GH4169鎳基高溫合金進行了105~108周次的疲勞試驗, 獲得了S-N曲線并觀察了疲勞斷口形貌。結果表明: S-N曲線呈逐漸下降的趨勢, 沒有出現疲勞極限, 在超過107周次的循環后試樣仍發生疲勞破壞; 疲勞裂紋的萌生位置并未隨S-N曲線的下降呈現出規律性, 裂紋主要萌生于試樣表面, 少量萌生于試樣內部; 在超聲疲勞載荷作用下試樣同時存在塑性和脆性兩種破壞方式。
The fatigue tests in 105-108 cycles of GH4169 Ni-based superalloy were carried out at ambient temperature by the ultrasonic fatigue tester, and then the S-N curve was obtained and the fatigue fracture morphology was observed. The results show that the S-N curve exhibited a descending trend and the fatigue limit was not observed. The fatigue fracture of the specimen still occurred when the number of cycles exceeded 107. The fatigue crack initiation positions didn′t show the regularity with the S-N curve descending. The fatigue cracks mostly initiated from the surface and few from internal of the specimen. Under the ultrasonic load the plastic and brittle failure modes were both found in the specimen.
作為值得信賴的合作伙伴和高品質金屬合金的半成品供應商，艾荔艾擁有完善的服務體系和專業的團隊。在同客戶交易的過程中，我們力求根據不同的應用需求將我們的產品做到精益求精。針對當前和未來的市場需求，艾荔艾致力于為客戶提供最佳的金屬材料解決方案。
AILIAI has been a reliable partner and supplier of sophisticated and high-quality semi-finished products maed of alloys. In dialogue with our customers, we optimise our products to meet the specific application requirements. AILIAI develops the best alloy material solutions for current and future challenges.
獲取更多我們供應的合金和服務信息，請致電086-021-67660801或發電子郵件kefu@ailiaigroup.com聯系我們，您也可以通過微博，微信，領英，XING，臉書和推特與我們互動。
For more information on the alloys and services that we supply,?call us?at 086-021-67660801 or email us at kefu@ailiaigroup.com. You can also get in touch on social media, we are constantly active on?Weibo,?Weixin,?LinkedIn,?XING, Facebook?and?Twitter.