拉伸保載對2.25Cr1MoV鋼高溫低周疲勞行為的影響
發布人：上海艾荔艾合金股份有限公司www.shailiai.cn
更新時間：2016-03-31
利用液壓疲勞試驗機, 采用軸向應變控制方法在455 ℃下對2.25Cr1MoV鋼進行高溫低周疲勞試驗, 通過在峰值應變拉伸時保載0,60,600 s, 研究了拉伸保載時間對該鋼低周疲勞行為的影響, 并用掃描電鏡對斷口形貌進行了觀察。
拉伸保載對2.25Cr1MoV鋼高溫低周疲勞行為的影響Effect of Tensile Holding on High Temperature Low Cycle Fatigue Behavior of 2.25Cr1MoV Steel利用液壓疲勞試驗機, 采用軸向應變控制方法在455 ℃下對2.25Cr1MoV鋼進行高溫低周疲勞試驗, 通過在峰值應變拉伸時保載0,60,600 s, 研究了拉伸保載時間對該鋼低周疲勞行為的影響, 并用掃描電鏡對斷口形貌進行了觀察。結果表明: 2.25Cr1MoV鋼呈明顯的循環軟化特性, 拉伸保載會明顯降低循環應力幅, 但保載時間對循環應力幅的影響不大; 拉伸保載使該鋼的疲勞壽命降低, 但保載時間超過60 s后, 疲勞壽命基本不受保載時間的影響; 拉伸保載沒有改變試驗鋼的疲勞斷裂模式。
High temperature low cycle fatigue test was carried out on 2.25Cr1MoV steel by using a hydraulic fatigue testing system under strain-controlled mode at 455 ℃. Different tensile hold time (0, 60, 600 s) was imposed at peak strain to study the effect of tensile holding load time on low cycle fatigue behavior of the steel. The fracture morphology of the steel was observed by scanning electron microscopy. The results reveal that the steel showed cyclic softening characteristics. The applied tensile holding load caused the stress amplitude obviously reduced, but the holding load time had little effect on cyclic stress amplitude. The fatigue life of the steel decreased because of tensile holding, but the life changed little when holding time exceeded 60 s.The fracture mode was not changed by the tensile holding load.
作為值得信賴的合作伙伴和高品質金屬合金的半成品供應商，艾荔艾擁有完善的服務體系和專業的團隊。在同客戶交易的過程中，我們力求根據不同的應用需求將我們的產品做到精益求精。針對當前和未來的市場需求，艾荔艾致力于為客戶提供最佳的金屬材料解決方案。
AILIAI has been a reliable partner and supplier of sophisticated and high-quality semi-finished products maed of alloys. In dialogue with our customers, we optimise our products to meet the specific application requirements. AILIAI develops the best alloy material solutions for current and future challenges.
獲取更多我們供應的合金和服務信息，請致電086-021-67660801或發電子郵件kefu@ailiaigroup.com聯系我們，您也可以通過微博，微信，領英，XING，臉書和推特與我們互動。
For more information on the alloys and services that we supply,?call us?at 086-021-67660801 or email us at kefu@ailiaigroup.com. You can also get in touch on social media, we are constantly active on?Weibo,?Weixin,?LinkedIn,?XING, Facebook?and?Twitter.