通過調(diào)整焊接熱輸入研究了 Q460 低合金高強鋼 CO2 氣體保護藥芯焊接接頭的組織及其對不同溫度下動態(tài)斷裂韌性(JId)的影響規(guī)律, 探究了影響接頭動態(tài)斷裂行為的機理.
Q460鋼焊接接頭組織及動態(tài)斷裂行為的研究STUDY ON MICROSTRUCTURE AND DYNAMIC FRACTURE BEHAVIOR?OF Q460 STEEL WELDING JOINTS?通過調(diào)整焊接熱輸入研究了 Q460 低合金高強鋼 CO2 氣體保護藥芯焊接接頭的組織及其對不同溫度下動態(tài)斷裂韌性(JId)的影響規(guī)律, 探究了影響接頭動態(tài)斷裂行為的機理. 結(jié)果表明, 低熱焊接輸入的接頭熔合區(qū)(FZ)柱狀晶界面處存在仿晶界型鐵素體; 隨熱輸入增加, FZ 柱狀晶形態(tài)特征逐漸減弱、仿晶界鐵素體消失, FZ 以針狀鐵素體組織為主, 且隨熱輸入的增加針狀鐵素體平均尺寸增大. 在室溫至-70 ℃范圍內(nèi), 中等熱輸入的焊接接頭均表現(xiàn)出優(yōu)異的動態(tài)斷裂韌性, 而低熱輸入的接頭動態(tài)斷裂韌性值最低. 隨溫度由室溫降低至-70 ℃, Q460 鋼焊接接頭動態(tài)斷裂機制發(fā)生了由延性斷裂逐漸向解理脆性斷裂的轉(zhuǎn)變. 低熱輸入焊接接頭 FZ 柱狀晶界面具有平面生長特征的仿晶界鐵素體, 易誘發(fā)低溫下裂紋沿晶快速擴展. 研究發(fā)現(xiàn)細小針狀鐵素體組織, 在低溫動態(tài)斷裂過程中, 由于可有效地阻礙裂紋擴展, 成為其維持高動態(tài)斷裂韌性的要因。
Effects of welding heat input on the microstructure and dynamic fracture toughness (JId) of the CO2?shielded arc welded joints of Q460 high strength low alloy steel were investigated. The mechanism of effects on?the dynamic facture behavior of the welded joint was also discussed. The results showed that there existed the?allotriomorphic ferrite at the columnar interface in the fusion zone of welded joint under the condition of low heat?input. The morphological characteristics of columnar crystal in the fusion zone gradually decreased and the?allotriomorphic ferrite disappeared as the heat input increased. The fusion zone was mainly composed of acicular?ferrite, and its average size increased with increasing heat input. The welded joint exhibited the optimal dynamic?fracture toughness under the condition of medium heat input while it showed the lowest value under low heat?input within the temperature range of -70 ℃ to room temperature. When the temperature decreased from room?temperature to -70 ℃, the dynamic fracture mechanism of Q460 welded joint changed from ductile fracture to?brittle cleavage fracture. Under the condition of low heat input, the allotriomorphic ferrite characterized by the?planar growth at the columnar interface in the fusion zone of welded joint can lead to the rapid intergranular crack?propagation at low temperature. The fine acicular ferrite in the fusion zone of the welding joint obtained at?medium heat input which can hinder the crack propagation during the dynamic fracture at low temperature to the?greatest extent is the reason why the welded joint exhibits high dynamic fracture toughness.?
作為值得信賴的合作伙伴和高品質(zhì)金屬合金的半成品供應商，艾荔艾擁有完善的服務體系和專業(yè)的團隊。在同客戶交易的過程中，我們力求根據(jù)不同的應用需求將我們的產(chǎn)品做到精益求精。針對當前和未來的市場需求，艾荔艾致力于為客戶提供最佳的金屬材料解決方案。
AILIAI has been a reliable partner and supplier of sophisticated and high-quality semi-finished products maed of alloys. In dialogue with our customers, we optimise our products to meet the specific application requirements. AILIAI develops the best alloy material solutions for current and future challenges.
獲取更多我們供應的合金和服務信息，請致電086-021-67660801或發(fā)電子郵件kefu@ailiaigroup.com聯(lián)系我們，您也可以通過微博，微信，領英，XING，臉書和推特與我們互動。
For more information on the alloys and services that we supply,?call us?at 086-021-67660801 or email us at kefu@ailiaigroup.com. You can also get in touch on social media, we are constantly active on?Weibo,?Weixin,?LinkedIn,?XING, Facebook?and?Twitter.