熱擠壓態FGH96粉末冶金高溫合金的顯微組織與力學性能
發布人：上海艾荔艾合金股份有限公司www.shailiai.cn
更新時間：2016-03-04
以熱擠壓態鎳基粉末冶金高溫合金FGH96為研究對象，研究該合金橫向(垂直于擠壓方向)和縱向(沿擠壓方向)試樣的顯微組織及力學性能，分析斷裂機制和變形后的顯微組織。
熱擠壓態FGH96粉末冶金高溫合金的顯微組織與力學性能Microstructure and mechanical properties of hot extruded FGH96 powder metallurgy superalloy?以熱擠壓態鎳基粉末冶金高溫合金FGH96為研究對象，研究該合金橫向(垂直于擠壓方向)和縱向(沿擠壓方向)試樣的顯微組織及力學性能，分析斷裂機制和變形后的顯微組織。結果表明：FGH96合金橫向及縱向試樣均為無明顯織構的等軸晶組織，且平均晶粒尺寸及γ′相體積分數基本一致。在應變速率1×10-4?s-1時，橫向和縱向拉伸試樣抗拉強度在25~650 ℃溫度區間內隨溫度升高緩慢降低，當溫度高于650 ℃時，抗拉溫度下降速率顯著增加；且橫向試樣的抗拉強度低于相同實驗條件下縱向試樣的抗拉強度，差值為150~200 MPa；失效機制為從室溫條件下的穿晶斷裂轉變為混合斷裂模式，橫向試樣的轉變溫度為400 ℃左右，縱向試樣的轉變溫度約為650 ℃；橫向試樣變形后，顯微組織有高密度的位錯纏結及層錯；縱向試樣拉伸斷裂后，顯微組織則主要為孿晶及位錯與γ′相的交互作用。
The deformed microstructure and mechanical properties of hot extruded nickel base P/M superalloy FGH96 were investigated. The transverse direction was defined as being vertical to the direction of hot extrusion, and the longitudinal direction was parallel to that of extrusion. The results indicate that both transverse and longitudinal specimens show equiaxed metallographic microstructure without obvious texture, and the average grain size as well as volume fraction of γ′ precipitation are out of distinct difference. Furthermore, under the condition of strain rate of 1×10-4?s-1?, the ultimate tensile strength of both transverse and longitudinal direction specimens of FGH96 superalloys decreases slightly with the temperature elevating from 25 ℃to 650 ℃, while drops sharply when the temperature is higher than 650 ℃. However, the ultimate tensile strength of transverse specimens is lower than that of longitudinal samples under the same test conditions. The failure mechanisms show a transition from transgranular fracture at 25 ℃ to a mixed mode which includes both transgranular facture and intergranular fracture at higher temperature. The transition temperature of transverse specimens is roughly 400 ℃, while that of longitudinal specimens is around 650 ℃. Tangled dislocations and stacking faults exist clearly in the deformed transverse samples, and it is mainly the twin and interaction between dislocations and γ′ precipitations that occur in the longitudinal specimens after tensile deformation.
作為值得信賴的合作伙伴和高品質金屬合金的半成品供應商，艾荔艾擁有完善的服務體系和專業的團隊。在同客戶交易的過程中，我們力求根據不同的應用需求將我們的產品做到精益求精。針對當前和未來的市場需求，艾荔艾致力于為客戶提供最佳的金屬材料解決方案。
AILIAI has been a reliable partner and supplier of sophisticated and high-quality semi-finished products maed of alloys. In dialogue with our customers, we optimise our products to meet the specific application requirements. AILIAI develops the best alloy material solutions for current and future challenges.
獲取更多我們供應的合金和服務信息，請致電086-021-67660801或發電子郵件kefu@ailiaigroup.com聯系我們，您也可以通過微博，微信，領英和推特與我們互動。
For more information on the alloys and services that we supply,?call us?at 086-021-67660801 or email us at kefu@ailiaigroup.com. You can also get in touch on social media, we are constantly active on?Weibo,?Weixin,?LinkedIn?and?Twitter.