研究采用斜軋穿孔及冷擴成形方法制備直徑大于130 mm的大口徑Ti-75無縫管材的可行性。分別測試穿孔管坯和冷擴后管材的金相組織、力學性能及沿管材軸向方向的裂紋情況。
Ti-75穿孔管坯的冷擴成形Cold expansion forming of Ti-75 perforated tube研究采用斜軋穿孔及冷擴成形方法制備直徑大于130 mm的大口徑Ti-75無縫管材的可行性。分別測試穿孔管坯和冷擴后管材的金相組織、力學性能及沿管材軸向方向的裂紋情況。結果表明：采用斜軋穿孔方式可以制備Ti-75合金大口徑無縫管材且擁有較好的塑性；在室溫下，進行冷擴，在擴徑率小于15%時，可得到抗拉強度為780 MPa，屈服強度為685 MPa，伸長率為13.5%，斷面收縮率為55%的管坯，且不出現擴裂等情況。
The feasibility of preparation of large-diameter seamless pipe of Ti-75 alloy using rotary piercing and cold expansion method. The microstructure, mechanical properties and crack along the pipe axial direction of the situation of the piercing tube and cold-expanded pipe were tested. The results show that Ti-75 large diameter alloy seamless pipe can be prepared using the rotary piercing method and it has a good plasticity. At room temperature, when the expansion of diameter is less than 15%, the tube with tensile strength of 780 MPa, yield strength of 685 MPa, elongation percentage of 13.5% and contraction of area of 55% can be obtained by cold expansion forming. There is no extending cleft in the tube.
作為值得信賴的合作伙伴和高品質金屬合金的半成品供應商，艾荔艾擁有完善的服務體系和專業的團隊。在同客戶交易的過程中，我們力求根據不同的應用需求將我們的產品做到精益求精。針對當前和未來的市場需求，艾荔艾致力于為客戶提供最佳的金屬材料解決方案。
AILIAI has been a reliable partner and supplier of sophisticated and high-quality semi-finished products maed of alloys. In dialogue with our customers, we optimise our products to meet the specific application requirements. AILIAI develops the best alloy material solutions for current and future challenges.
獲取更多我們供應的合金和服務信息，請致電086-021-67660801或發電子郵件kefu@ailiaigroup.com聯系我們，您也可以通過微博，微信，領英和推特與我們互動。
For more information on the alloys and services that we supply,?call us?at 086-021-67660801 or email us at kefu@ailiaigroup.com. You can also get in touch on social media, we are constantly active on?Weibo,?Weixin,?LinkedIn?and?Twitter.