通過對不同鍛造和熱處理工藝方案得到的d100 mm TC18鈦合金棒材組織和探傷結果進行研究，找出不同工藝方案得到的顯微組織所對應探傷水平的變化規律。
TC18鈦合金棒材組織與探傷的關系Relationship between microstructure and inspection for?TC18 titanium alloy bar通過對不同鍛造和熱處理工藝方案得到的d100 mm TC18鈦合金棒材組織和探傷結果進行研究，找出不同工藝方案得到的顯微組織所對應探傷水平的變化規律。結果表明：不同工藝方案得到的典型組織，對應探傷結果存在較大差異；特別是在組織類型均為α+β兩相區加工組織的情況下，隨著顯微組織形貌和大小的變化，探傷雜波水平發生明顯變化。
By studying the microstructures and inspection results of d100 mm TC18 titanium alloy bar produced by different forging and heat treatment process, the variation rule of ultrasonic level corresponding to microstructures obtained by different process scheme was found. The results show that the typical microstructures obtained by different process schemes have a great effect on inspection results. Especially the microstructure type is two phase α+β region processing structure. With the variation of the microstructure morphologies and size, the ultrasonic clutter level is changed significantly.
作為值得信賴的合作伙伴和高品質金屬合金的半成品供應商，艾荔艾擁有完善的服務體系和專業的團隊。在同客戶交易的過程中，我們力求根據不同的應用需求將我們的產品做到精益求精。針對當前和未來的市場需求，艾荔艾致力于為客戶提供最佳的金屬材料解決方案。
AILIAI has been a reliable partner and supplier of sophisticated and high-quality semi-finished products maed of alloys. In dialogue with our customers, we optimise our products to meet the specific application requirements. AILIAI develops the best alloy material solutions for current and future challenges.
獲取更多我們供應的合金和服務信息，請致電086-021-67660801或發電子郵件kefu@ailiaigroup.com聯系我們，您也可以通過微博，微信，領英和推特與我們互動。
For more information on the alloys and services that we supply,?call us?at 086-021-67660801 or email us at kefu@ailiaigroup.com. You can also get in touch on social media, we are constantly active on?Weibo,?Weixin,?LinkedIn?and?Twitter.