氮氣氣氛下激光切割對TC11鈦合金組織及焊接接頭性能的影響
發布人：上海艾荔艾合金股份有限公司www.shailiai.cn
更新時間：2016-01-26
對TC11鈦合金在氮氣氛下進行激光切割，并在氮氣氛下進行熱處理，對比熱處理前后的顯微組織和硬度，確定熱影響層深度。去除激光切割影響層后進行電子束焊接，比較研究未激光切割和激光切割焊接接頭的拉伸和疲勞性能。
氮氣氣氛下激光切割對TC11鈦合金組織及焊接接頭性能的影響Effect of laser cutting in nitrogen atmosphere on microstructure of TC11 titanium alloy and properties of welding joints對TC11鈦合金在氮氣氛下進行激光切割，并在氮氣氛下進行熱處理，對比熱處理前后的顯微組織和硬度，確定熱影響層深度。去除激光切割影響層后進行電子束焊接，比較研究未激光切割和激光切割焊接接頭的拉伸和疲勞性能。結果表明：激光切割熱影響層深度在2~3 mm之間；未激光切割和激光切割TC11鈦合金焊接接頭低周疲勞性能未見明顯差異，但是激光切割后的焊接接頭抗拉強度和伸長率相對未激光切割焊接接頭分別低45 MPa和3%左右。
TC11 titanium alloy plates were cut by laser and then heat treated in nitrogen atmosphere. The microstructure and microhardness of the surface layers affected by laser cutting were investigated before and after heat treatment. The depth of the heat influence zones by laser cutting was tested. The influenced layers by laser cutting were removed and then the plates were joined by electron beam welding. The effect of laser cutting on the tensile and fatigue properties of the welding joints of TC11 titanium alloy was studied. The results show that the depth of the heat influence zones by laser cutting is in the range of 2 mm to 3 mm. The effect of laser cutting on the low-cycle fatigue property of the welding joint of TC11 titanium alloy is slight, but laser cutting make the tensile strength and elongation percentage decrease by 45 MPa and 3%, respectively.
作為值得信賴的合作伙伴和高品質金屬合金的半成品供應商，艾荔艾擁有完善的服務體系和專業的團隊。在同客戶交易的過程中，我們力求根據不同的應用需求將我們的產品做到精益求精。針對當前和未來的市場需求，艾荔艾致力于為客戶提供最佳的金屬材料解決方案。
AILIAI has been a reliable partner and supplier of sophisticated and high-quality semi-finished products maed of alloys. In dialogue with our customers, we optimise our products to meet the specific application requirements. AILIAI develops the best alloy material solutions for current and future challenges.
獲取更多我們供應的合金和服務信息，請致電086-021-67660801或發電子郵件kefu@ailiaigroup.com聯系我們，您也可以通過微博，微信，領英和推特與我們互動。
For more information on the alloys and services that we supply,?call us?at 086-021-67660801 or email us at kefu@ailiaigroup.com. You can also get in touch on social media, we are constantly active on?Weibo,?Weixin,?LinkedIn?and?Twitter.