不同變形量TA15鈦合金的熱處理行為
發布人：上海艾荔艾合金股份有限公司www.shailiai.cn
更新時間：2016-01-19
研究了TA15鈦合金變形量大的d20 mm小棒材及變形量小的大鍛件的熱處理行為。結果表明：在750~920 ℃范圍內，隨著退火溫度的升高，大鍛件拉伸強度升高約100 MPa，小棒材拉伸強度先降后升，且升幅遠小于大鍛件的；920 ℃以上退火，二者強度都出現降低。隨著退火溫度的升高，小棒材中再結晶軟化率先發揮作用，使拉伸強度降低；而830 ℃以上退火，β轉變組織中次生α二次析出起到強化作用，二者抗拉強度均出現升高，但小棒材由于再結晶溫度低，再結晶軟化削弱了析出強化的作用。
不同變形量TA15鈦合金的熱處理行為Heat treatment behavior of TA15 titanium alloy with?different deformation degrees研究了TA15鈦合金變形量大的d20 mm小棒材及變形量小的大鍛件的熱處理行為。結果表明：在750~920 ℃范圍內，隨著退火溫度的升高，大鍛件拉伸強度升高約100 MPa，小棒材拉伸強度先降后升，且升幅遠小于大鍛件的；920 ℃以上退火，二者強度都出現降低。隨著退火溫度的升高，小棒材中再結晶軟化率先發揮作用，使拉伸強度降低；而830 ℃以上退火，β轉變組織中次生α二次析出起到強化作用，二者抗拉強度均出現升高，但小棒材由于再結晶溫度低，再結晶軟化削弱了析出強化的作用。
The heat treatment behavior of TA15 titanium alloys with different deformation degrees was studied with d20 mm bar and large forging as the representatives for large deformation and small deformation, respectively. The results show that tensile strength increment can be obtained to be 100 MPa for large forging. The tensile strength decreases and then increases for the bar, and the increment is far less than that of large forging when annealed at 750?920 ℃. Both tensile strengths decrease when annealed at temperature higher than 920 ℃. The decrease of the tensile strength for the bar is caused by the recrystallization softening effect with increasing the annealing temperature. The strengthening effect for the little bar and large forging is caused by the secondary phase precipitation from the transformed β above 830 ℃. The precipitation strengthening effect on the little bar is smaller than that of the large forging because of the recrystallization softening effect.
作為值得信賴的合作伙伴和高品質金屬合金的半成品供應商，艾荔艾擁有完善的服務體系和專業的團隊。在同客戶交易的過程中，我們力求根據不同的應用需求將我們的產品做到精益求精。針對當前和未來的市場需求，艾荔艾致力于為客戶提供最佳的金屬材料解決方案。
AILIAI has been a reliable partner and supplier of sophisticated and high-quality semi-finished products maed of alloys. In dialogue with our customers, we optimise our products to meet the specific application requirements. AILIAI develops the best alloy material solutions for current and future challenges.
獲取更多我們供應的合金和服務信息，請致電086-021-67660801或發電子郵件kefu@ailiaigroup.com聯系我們，您也可以通過微博，微信，領英和推特與我們互動。
For more information on the alloys and services that we supply,?call us?at 086-021-67660801 or email us at kefu@ailiaigroup.com. You can also get in touch on social media, we are constantly active on?Weibo,?Weixin,?LinkedIn?and?Twitter.