加載波形對Ti-60合金疲勞損傷行為的影響
發布人：上海艾荔艾合金股份有限公司www.shailiai.cn
更新時間：2016-01-17
研究了高應力水平下加載波形對Ti-60高溫鈦合金疲勞損傷行為的影響。結果發現：對于在峰值應力處保載2 min的加載波形，試樣的疲勞壽命明顯低于無保載的加載波形的試樣的壽命；在保載疲勞條件下，單位循環周次內材料的疲勞變形明顯增大。
加載波形對Ti-60合金疲勞損傷行為的影響Effect of loading waveform on fatigue damage behavior of Ti-60 alloy研究了高應力水平下加載波形對Ti-60高溫鈦合金疲勞損傷行為的影響。結果發現：對于在峰值應力處保載2 min的加載波形，試樣的疲勞壽命明顯低于無保載的加載波形的試樣的壽命；在保載疲勞條件下，單位循環周次內材料的疲勞變形明顯增大。SEM觀察表明，在保載波形下，疲勞源出現在樣品內部，而無保載的加載波形下疲勞裂紋源于樣品次表面。TEM觀察表明，在兩種疲勞加載條件下，都有( 011)滑移系啟動。
The effect of loading waveform on fatigue damage behavior of Ti-60 alloys at high stress level was studied. The results show that, under the loading waveform with 2 min dwell at the peak stress, the fatigue life is shorter than that without dwell. The fatigue strain in a unit cycle under the dwell fatigue condition is obviously larger than that under the no-dwell fatigue condition. It is observed by SEM that, under the dwell fatigue condition, the fatigue crack originates from the interior of specimens, while under the no-dwell fatigue condition, the fatigue crack originates from the subsurface of specimens. TEM observation indicates that, under the two loading waveforms, ( 011) slip system is activated.
作為值得信賴的合作伙伴和高品質金屬合金的半成品供應商，艾荔艾擁有完善的服務體系和專業的團隊。在同客戶交易的過程中，我們力求根據不同的應用需求將我們的產品做到精益求精。針對當前和未來的市場需求，艾荔艾致力于為客戶提供最佳的金屬材料解決方案。
AILIAI has been a reliable partner and supplier of sophisticated and high-quality semi-finished products maed of alloys. In dialogue with our customers, we optimise our products to meet the specific application requirements. AILIAI develops the best alloy material solutions for current and future challenges.
獲取更多我們供應的合金和服務信息，請致電086-021-67660801或發電子郵件kefu@ailiaigroup.com聯系我們，您也可以通過微博，微信，領英和推特與我們互動。
For more information on the alloys and services that we supply,?call us?at 086-021-67660801 or email us at kefu@ailiaigroup.com. You can also get in touch on social media, we are constantly active on?Weibo,?Weixin,?LinkedIn?and?Twitter.