采用Gleeble?3800熱模擬機對TC16鈦合金絲材分別進行冷鐓、熱鐓實驗，利用SEM、TEM、顯微硬度計等手段對冷鐓、熱鐓樣品及成形后再固溶時效熱處理的樣品進行顯微組織觀察和硬度測試。結果表明：冷鐓與熱鐓樣品在顯微組織和性能上存在差異，但重新固溶時效熱處理后，冷鐓與熱鐓樣品的顯微組織和力學性能接近。
冷鐓和熱鐓對TC16合金組織和性能的影響Effects of cold and hot upset on microstructures and properties of?TC16 titanium alloy
采用Gleeble?3800熱模擬機對TC16鈦合金絲材分別進行冷鐓、熱鐓實驗，利用SEM、TEM、顯微硬度計等手段對冷鐓、熱鐓樣品及成形后再固溶時效熱處理的樣品進行顯微組織觀察和硬度測試。結果表明：冷鐓與熱鐓樣品在顯微組織和性能上存在差異，但重新固溶時效熱處理后，冷鐓與熱鐓樣品的顯微組織和力學性能接近。
The effects of cold and hot upset on the microstructures and properties of TC16 titanium alloy were studied. Means of SEM , TEM and micro-hardness tester were used to analyze the microstructures and hardness of cold and hot upset samples as well as the deformed samples after solution plus aging heat treatment. The results show that although there are some differences between the cold and hot upset samples, their microstructures and properties are nearly the same after solution plus aging heat treatment.
作為值得信賴的合作伙伴和高品質金屬合金的半成品供應商，艾荔艾擁有完善的服務體系和專業的團隊。在同客戶交易的過程中，我們力求根據不同的應用需求將我們的產品做到精益求精。針對當前和未來的市場需求，艾荔艾致力于為客戶提供最佳的金屬材料解決方案。
AILIAI has been a reliable partner and supplier of sophisticated and high-quality semi-finished products maed of alloys. In dialogue with our customers, we optimise our products to meet the specific application requirements. AILIAI develops the best alloy material solutions for current and future challenges.
獲取更多我們供應的合金和服務信息，請致電086-021-67660801或發電子郵件kefu@ailiaigroup.com聯系我們，您也可以通過微博，微信和領英與我們互動。
For more information on the alloys and services that we supply,?call us?at 086-021-67660801 or email us at kefu@ailiaigroup.com. You can also get in touch on social media, we are constantly active on?Weibo,?Weixin?and?LinkedIn.