熱軋變形對TB-13合金組織和織構的影響
發布人：上海艾荔艾金屬材料有限公司www.jshcn.cn
更新時間：2015-12-27
采用光學顯微鏡和X射線衍射儀分析TB-13合金在不同熱軋變形條件下組織和織構的演變規律。
熱軋變形對TB-13合金組織和織構的影響Influence of hot rolling deformation on microstructure and?texture of TB-13 alloy
采用光學顯微鏡和X射線衍射儀分析TB-13合金在不同熱軋變形條件下組織和織構的演變規律。結果表明：TB-13合金在變形量小于50%的熱軋過程中只發生動態回復，當變形量增加到59%時，該合金發生動態再結晶，且隨著變形量的增加，動態再結晶程度逐漸增大，細小的再結晶亞晶粒逐漸取代原始等軸狀β晶粒從而使組織細化，動態再結晶是該合金熱軋過程中主要的細化機制。同時，熱軋變形使得該合金形成以旋轉立方取向{001}＜110＞織構和Goss取向{110}＜001＞織構為主的多種織構，且隨著變形量的增大，晶粒取向由Goss取向向旋轉立方取向轉移。
The evolutions of microstructure and texture for TB-13 alloy during hot rolling were investigated by optical microscopy and X-ray diffracometry. The results show that the deformation mechanism is dynamic recovery in TB-13 alloy when the deformation reduction is less than 50%. When the deformation reduction is 59%, dynamic recrystallization occurs and the volume fraction of dynamic recrystallization increases with the increase of the deformation reduction. The equiaxed β grains are substituted for the recrystal grains, which leads to microstructure refinement. This indicates that the refinement mechanism is dynamic recrystallization. The main texture components of TB-13 alloy after hot rolling deformation are {001} ＜110＞ and {110} ＜001＞ textures. The orientation of grain changes from Goss orientation to rotating cube orientation when the deformation reduction increases.
作為值得信賴的合作伙伴和高品質金屬合金的半成品供應商，艾荔艾擁有完善的服務體系和專業的團隊。在同客戶交易的過程中，我們力求根據不同的應用需求將我們的產品做到精益求精。針對當前和未來的市場需求，艾荔艾致力于為客戶提供最佳的金屬材料解決方案。
AILIAI has been a reliable partner and supplier of sophisticated and high-quality semi-finished products maed of alloys. In dialogue with our customers, we optimise our products to meet the specific application requirements. AILIAI develops the best alloy material solutions for current and future challenges.
獲取更多我們供應的合金和服務信息，請致電086-021-67660801或發電子郵件kefu@ailiaigroup.com聯系我們，您也可以通過微博和微信和我們互動。
For more information on the alloys and services that we supply,?call us?at 086-021-67660801 or email us at kefu@ailiaigroup.com. You can also get in touch on social media, we are constantly active on?Weibo?and?Weixin.