通過OM、SEM、X射線衍射、DSC差熱分析和室溫拉伸性能測試，研究固溶處理對7150鋁合金擠壓板帶組織和力學性能的影響。
固溶處理對7150鋁合金組織和力學性能的影響Effect of solution treatment on microstructures and?mechanical properties of 7150 aluminum alloy
通過OM、SEM、X射線衍射、DSC差熱分析和室溫拉伸性能測試，研究固溶處理對7150鋁合金擠壓板帶組織和力學性能的影響。結果表明：合金固溶處理溫度越高，時間越長，粗大第二相溶解越多；合金在480℃進行固溶處理時，出現過燒組織，雙級固溶處理制度沒有提高本合金開始出現過燒組織的溫度；隨著合金固溶處理時間的延長，組織出現粗化和再結晶的趨勢；本合金適合采用475 ℃，2 h的單級固溶制度，經(475 ℃，2 h) + (120 ℃，24 h)固溶?峰時效處理后，合金抗拉強度、屈服強度和伸長率分別為650 MPa、600 MPa和13.5%。
The effects of solution treatment on the microstructures and mechanical properties of 7150 aluminum alloy extrusion plate were studied by OM, SEM, XRD, DSC and room temperature tensile test. The results show that the coarse second phase dissolves more adequately when the alloy is solution treated at higher temperature for longer time. The overheated structure appears in alloys when quenched at 480 ℃, and the temperature at which overheated structure appears cannot be enhanced by two-stage solution. The trend of microstructure coarsening and recrystallization appears with prolongating the solution time. The suited solution of the alloy is single-stage solution of 475 ℃, 2 h. After solution and peak aging of (475 ℃, 2 h)+(120 ℃, 24 h), the ultimate tensile strength, yield strength and elongation are 650 MPa, 600 MPa and 13.5%, respectively.
作為值得信賴的合作伙伴和高品質金屬合金的半成品供應商，艾荔艾擁有完善的服務體系和專業的團隊。在同客戶交易的過程中，我們力求根據不同的應用需求將我們的產品做到精益求精。針對當前和未來的市場需求，艾荔艾致力于為客戶提供最佳的金屬材料解決方案。
AILIAI has been a reliable partner and supplier of sophisticated and high-quality semi-finished products maed of alloys. In dialogue with our customers, we optimise our products to meet the specific application requirements. AILIAI develops the best alloy material solutions for current and future challenges.
獲取更多我們供應的合金和服務信息，請致電086-021-67660801或發電子郵件kefu@ailiaigroup.com聯系我們，您也可以通過微博和微信和我們互動。
For more information on the alloys and services that we supply,?call us?at 086-021-67660801 or email us at kefu@ailiaigroup.com. You can also get in touch on social media, we are constantly active on?Weibo?and?Weixin.