固溶時(shí)間對(duì)ZA72鎂合金顯微組織及力學(xué)性能的影響
發(fā)布人：上海艾荔艾金屬材料有限公司www.jshcn.cn
更新時(shí)間：2015-12-13
利用光學(xué)顯微鏡、X射線衍射儀、掃描電鏡和力學(xué)萬能試驗(yàn)機(jī)研究ZA72鎂合金在不同固溶時(shí)間下T6處理后的顯微組織和力學(xué)性能。
固溶時(shí)間對(duì)ZA72鎂合金顯微組織及力學(xué)性能的影響Effects of different solution time on microstructure and?mechanical properties of ZA72 magnesium alloy
利用光學(xué)顯微鏡、X射線衍射儀、掃描電鏡和力學(xué)萬能試驗(yàn)機(jī)研究ZA72鎂合金在不同固溶時(shí)間下T6處理后的顯微組織和力學(xué)性能。結(jié)果表明：ZA72鎂合金主要由α-Mg 和分布在晶界的連續(xù)粗大的Mg32(Al, Zn)49和Mg7Zn3相組成，經(jīng)過固溶處理后第二相呈細(xì)小的顆粒狀分布在晶界和晶粒上，隨著固溶時(shí)間的增加，第二相的尺寸和數(shù)量逐漸減小；經(jīng)T6處理后，細(xì)小、彌散的白色點(diǎn)狀強(qiáng)化相在晶界和晶粒內(nèi)部彌散析出，并且隨著固溶時(shí)間的增加，析出相的數(shù)量增加；通過T6處理后合金的力學(xué)性能有了明顯的改善，合金的抗拉強(qiáng)度和顯微硬度隨固溶時(shí)間的增加呈先上升后下降的趨勢(shì)，其中在固溶28 h后抗拉強(qiáng)度出現(xiàn)峰值308 MPa，相對(duì)于鑄態(tài)提高了52.4%。
The microstructure and mechanical properties of ZA72 magnesium alloy after T6 heat treatment with different solution times were investigated using optical microscope (OM), X-ray diffractometer (XRD), mechanical apparatus and scanning electron microscope (SEM). The results show that the ZA72 magnesium alloy mainly contains?α-Mg, bulky Mg32(Al,Zn)49?and Mg7Zn3?phases which distribute on the grain boundary continuously. After T4 heat treatment, the second phases are converted to fine particles, meanwhile the size and amount have decreased gradually with the solution time increasing. The fine and dispersible white dots precipitates separate out at the grain boundary and grain internal, in addition that the amount of precipitates increase with the solution time extending. The mechanical properties of alloy are obviously improved after T6 heat treatment, the tensile strength and micro-hardness show the trend of arising first and descending later. When the solution time is 28 h, the tensile strength reaches the peak value of 308 MPa, which increases by 52.4% compared with that of the as-cast alloy.
獲取更多我們供應(yīng)的合金和服務(wù)信息，請(qǐng)致電086-021-67660801或發(fā)電子郵件kefu@ailiaigroup.com聯(lián)系我們，您也可以通過微博和微信和我們互動(dòng)。
For more information on the alloys and services that we supply,?call us?at 086-021-67660801 or email us at kefu@ailiaigroup.com. You can also get in touch on social media, we are constantly active on?Weibo?and?Weixin.