滲注磷酸鹽對AZ31鎂合金疲勞裂紋擴展的影響
發布人：上海艾荔艾金屬材料有限公司www.jshcn.cn
更新時間：2015-12-08
交變載荷作用下在AZ31鎂合金疲勞裂紋尖端滲注磷酸鹽轉化液，研究磷酸鹽的沉積行為及其對AZ31鎂合金疲勞裂紋擴展速率的影響。采用掃描電鏡(SEM)、能譜儀(EDS)、X射線衍射儀(XRD)觀察分析裂紋尖端的形貌和物相組成，并采用貼應變片方法確定滲注磷酸鹽轉化液前后應力強度因子的變化。
滲注磷酸鹽對AZ31鎂合金疲勞裂紋擴展的影響Effects of immersing phosphate on?fatigue crack propagation in AZ31 magnesium alloy
交變載荷作用下在AZ31鎂合金疲勞裂紋尖端滲注磷酸鹽轉化液，研究磷酸鹽的沉積行為及其對AZ31鎂合金疲勞裂紋擴展速率的影響。采用掃描電鏡(SEM)、能譜儀(EDS)、X射線衍射儀(XRD)觀察分析裂紋尖端的形貌和物相組成，并采用貼應變片方法確定滲注磷酸鹽轉化液前后應力強度因子的變化。結果表明：滲注的磷酸鹽轉化液在AZ31鎂合金疲勞裂紋尖端形成Zn3(PO4)?4H2O及MgZnP2O7復合覆層，能改變疲勞裂紋尖端的應力大小和分布狀態，使應力強度因子降低約30%，從而有效地增強疲勞裂紋閉合效應，降低或延滯AZ31鎂合金疲勞裂紋的擴展。
Under alternate loads, a phosphate liquid was immersed into the fatigue crack tip of AZ31 magnesium alloy, the phosphate deposition behavior and effects of the phosphate film on the fatigue crack propagation rate at the fatigue crack tip of AZ31 magnesium alloy were investigated. The morphologies and phase constitutions of the phosphate deposition at the fatigue crack tip were characterized by scanning electron microscopy (SEM), energy spectrum analysis (EDS) and X-ray diffractometry (XRD), respectively. The stress-intensity factor values at the fatigue crack tip were compared with and without inmersing phosphate liquid by taking advantage of strain gauge. The results show that the phosphate( Zn3(PO4)?4H2O and MgZnP2O7) films can be formed at the fatigue crack tip of AZ31 alloy through inmersing phosphate liquid, and the stress magnitude and distribution change after inmersing phosphate liquid at the fatigue crack tip of AZ31 alloy. The stress-intensity factor value decreases by about 30%, which effectively improves the fatigue crack closure, and reduces or arrearage the fatigue crack propagation.
獲取更多我們供應的合金和服務信息，請致電086-021-67660801或發電子郵件kefu@ailiaigroup.com聯系我們，您也可以通過微博和微信和我們互動。
For more information on the alloys and services that we supply,?call us?at 086-021-67660801 or email us at kefu@ailiaigroup.com. You can also get in touch on social media, we are constantly active on?Weibo?and?Weixin.