Zn元素及時效工藝對2056鋁合金微觀組織和力學性能的影響
發(fā)布人：上海艾荔艾金屬材料有限公司www.jshcn.cn
更新時間：2015-10-21
通過顯微硬度測試、常規(guī)拉伸性能測試、DSC分析和透射電鏡觀察，研究少量Zn元素及時效工藝對2056鋁合金微觀組織與力學性能的影響。
Zn元素及時效工藝對2056鋁合金微觀組織和力學性能的影響Effects of Zn additions and aging process on microstructure and mechanical properties of 2056 aluminum alloy
通過顯微硬度測試、常規(guī)拉伸性能測試、DSC分析和透射電鏡觀察，研究少量Zn元素及時效工藝對2056鋁合金微觀組織與力學性能的影響。結果表明：在T6、T8和T3時效狀態(tài)下，2056合金的抗拉強度(σb)和屈服強度(σ0.2)均比不含Zn合金的高，而伸長率(δ)相差不大，這是因為Zn的添加形成富Zn 團簇，促進GPB區(qū)的形成，進一步促進S′相的析出，提高合金強度。2056合金在T6、T8峰時效態(tài)和T3態(tài)下的σb和σ0.2由大到小順序為T8，T3和T6，時效前的預變形形成大量位錯，由于位錯和溶質原子強烈的交互作用，形成大量的位錯塞積和纏結，增加了T3態(tài)合金的強度；在T8態(tài)下，大量的位錯成為S′相的形核點，使合金形成細小、密集和均勻彌散的S′相，其強度較T6和T3態(tài)的得到較大提高。
The effects of Zn additions and aging process on the microstructure and mechanical properties of 2056 aluminum alloy were investigated by micro-hardness test, tensile test, differential scanning calorimetry (DSC) and transmission electron microscopy (TEM). The results show that the tensile strength (σb) and yield strength (σ0.2) of 2056 aluminum alloy are higher than those of the alloy without Zn while the elongation is almost the same in T6, T8 and T3 temper. This is because with the addition of Zn, Zn-rich clusters form, which accelerates the precipitation of GPB zone and the precipitation of S′ phase further, thus improving the strength of the alloy. The order of σb?and σ0.2of 2056 aluminum alloy in T3, peak-aged T6 and T8 temper from large to small is T8, T3 and T6. The predeformation before aging makes plenty of dislocations form. Due to the strong interaction between the solute atoms and dislocations, there exists large quantity of dislocation pile-up while dislocations become tangled up, which improve the strength in T3 temper. In T8 temper, the dislocations become the precipitation sites of S′ phase, making fine, dense and uniform S′ phase in the matrix. The strength of the alloy in T8 temper improves a lot compared with that of T6 and T3 temper.
以上資料由上海艾荔艾金屬材料有限公司提供，歡迎新老客戶來電洽購。
本文來自上海艾荔艾金屬材料有限公司http://www.jshcn.cn，轉載請注明出處。