ZA27合金的熱變形及加工圖
發布人：上海艾荔艾金屬材料有限公司www.jshcn.cn
更新時間：2015-10-08
采用Gleeble?1500熱模擬實驗機進行熱壓縮試驗，研究ZA27合金的熱變形行為，在變形溫度為200~ 350 ℃、應變速率為0.01~5 s?1、工程應變為60%，基于Murty準則，建立ZA27合金的加工圖。
ZA27合金的熱變形及加工圖Hot deformation and processing map of ZA27 alloy
采用Gleeble?1500熱模擬實驗機進行熱壓縮試驗，研究ZA27合金的熱變形行為，在變形溫度為200~?? 350 ℃、應變速率為0.01~5 s?1、工程應變為60%，基于Murty準則，建立ZA27合金的加工圖。結果表明：流變應力隨變形溫度的升高而減小，隨應變速率的提高而增大；在變形溫度為200~210 ℃、應變速率為0.01~0.1 s?1和變形溫度為250~350 ℃、應變速率為1~5 s?1的2個區域內易產生流變失穩現象；動態再結晶是導致流變軟化及穩態流變的主要原因，ZA27合金的安全熱加工區域的變形溫度在250~350 ℃之間、應變速率在0.1~1 s?1之間。
The hot deformation behavior of ZA27 alloy were investigated by compressive tests on Gleeble?1500 thermal-mechanical simulating tester in the temperatures range of 200?350 ℃, strain rate range of 0.01?5 s?1?and engineering strain of 60%. Based on Murty criterion, the processing map for the ZA27 alloy was obtained. The results show that the flow stress decreases with the increase of temperature, while increases with the increase of strain rate. The flow instability regimes appear at two different regimes: at the temperature of 200?210 ℃and the strain of 0.01?0.1 s?1, as well as at the temperature of 250?350 ℃ and the strain rate of 1?5 s?1. The dynamic recrystallization is the main reason for flow softening and stable flow. The hot deformation of ZA27 alloy can be carried out safely in the region with a strain rate of 0.1?1 s?1?and temperature range of 250?350 ℃.
以上資料由上海艾荔艾金屬材料有限公司提供，歡迎新老客戶來電洽購。
本文來自上海艾荔艾金屬材料有限公司http://www.jshcn.cn，轉載請注明出處。