Al-6.5%Mg合金的半固態流變鑄造及其性能
發布人：上海艾荔艾金屬材料有限公司www.jshcn.cn
更新時間：2015-09-19
利用保溫電磁攪拌制備半固態漿料，對Al-6.5%Mg合金的半固態流變鑄造進行研究。實驗中對該合金的常壓鑄造、液態壓鑄和半固態壓鑄所得鑄件的顯微組織、力學性能和拉伸斷口進行分析比較。
Al-6.5%Mg合金的半固態流變鑄造及其性能Semi-solid rheocasting and performance of Al-6.5%Mg alloy
利用保溫電磁攪拌制備半固態漿料，對Al-6.5%Mg合金的半固態流變鑄造進行研究。實驗中對該合金的常壓鑄造、液態壓鑄和半固態壓鑄所得鑄件的顯微組織、力學性能和拉伸斷口進行分析比較。結果表明，常壓鑄造得到的Al-6.5%Mg合金組織為粗大的樹枝晶，力學性能較低；與常壓鑄造相比，液態壓鑄件的樹枝晶生長較為規則，枝晶得到細化，同時，液態壓鑄件的強度和塑性提高明顯；半固態壓鑄的顯微組織則為規則的球狀晶，與液態壓鑄相比，半固態壓鑄件的強度略有提高，表現出更好的塑性。
Semi-solid rheocasting of Al-6.5% Mg alloy was studied by using the method of thermal electromagnetic stirring to prepare semi-solid slurry. The microstructure, mechanical properties and tensile fracture of the castings under the conditions of constant pressure casting, liquid metal die-casting and semi-solid die-casting were compared. The results demonstrate that the Al-6.5%Mg alloy produced by conventional casting has coarse dendritic grains with low mechanical properties. Compared with constant pressure casting, the dendritic grains from liquid metal die-casting are more regular and finer, the strength and plasticity of liquid metal die-casting are improved. The microstructure in semi-solid die-casting shows regular spherical grains. Compared with liquid metal die-casting, the strength in semi-solid die-casting is slightly improved, and showing a better plasticity.
以上資料由上海艾荔艾金屬材料有限公司提供，歡迎新老客戶來電洽購。
本文來自上海艾荔艾金屬材料有限公司http://www.jshcn.cn，轉載請注明出處。