7475鋁合金陽極氧化膜表面-界面組織與特征Surface-interface structures and characteristics of anodic oxidation film on 7475 aluminium alloy

利用陽極氧化法在7475鋁合金表面制備一層氧化膜。通過SEM、EDS、XRD等手段分析其表面-界面形貌、化學元素組成和物相，對其表面和結合界面化學元素進行面掃描和線掃描分析，并對氧化膜界面結合形式進行表征。結果表明：陽極氧化膜主要是由Al和O元素組成，還含有板材中所不具備的C、K和S元素，主要來源于陽極氧化的電解液；生成的氧化膜為穩相α-Al₂O₃和亞穩相γ-Al₂O₃，其中以α-Al₂O₃為主；Al和O原子在氧化膜結合界面形成富集層，其界面為化合物型+擴散型形式。

The layer of oxide film was prepared on the surface of 7475 aluminum alloy by anodic oxidation method. The surface-interface morphologies, chemical element compositions and phases were analyzed by SEM, EDS and XRD, respectively, and the chemical elements of the surface and bonding interface were analyzed by plane scan and line scan, respectively, and the interface binding of oxide film was characterized. The results show that anodic oxide film is made up of Al and O elements and C, K and S elements from the anodic oxidation electrolyte of anodic oxidation film. The produced oxide film is composed of stationary phase α-Al₂O₃ and metastable phase γ-Al₂O₃, mainly includes α-Al₂O₃. The hierarchical enrichment phenomenon of Al and O atoms in the oxide film is produced after anodic oxidation, the bonding form of compound type + diffusion type forms at the interface.

全文下載：http://pan.baidu.com/s/1bnlVeDx